- product information
A fast drying zinc rich primer/topcoat based on an epoxy ester resin.
The product contains pure zinc and aluminium as pigment and provides cathodic protection.
Should be used as a single coat in light industrial exposures, corrosive environments and high humidity areas.
For use on damaged galvanized steel surfaces and is intended to be applied on small areas or for touch-up.
- technical specifications
Size 500ml For use on
New, bare steel, blasted steel or galvanized steel surfaces Appearance Sparkling Drying times 20°C/50% r.v. To touch
10 Minutes Drying times 20°C/50% r.v. To Recoat Within 2 hours or after 48 hours Binder Epoxy ester Heat Resistance 450°C (dry heat) Theoretical Coverage
1.2 m² per spay can at 35 μm dry
MPN 2117 GTIN
- • Sparkling aluminium finish (80% zinc, 10% alu)
- • Compromise between a protection and finish
- • For new, bare, rust free metal or galvanised steel
- • Resists 340 hours of salt spray testing (DIN)
- • Heat-resistant up to 450 °C
- • To handle after 1 hour (at 20°C)
Remove dirt, grease, oil, loose rust and all other surface contaminants by appropriate means.
Prime or spot prime with the recommended RUST-OLEUM Primers. Sand intact coatings to provide a proper key for adhesion.
The surface must be clean and dry during application.
DIRECTION FOR USE
Remove cover cap. Shake vigorously for at least one minute after the rattle of mixing ball is heard.
Shake frequently during use. Hold can at least 25 cm from surface.
Use back and forth motion keeping can parallel with surface. Ensure that can is in motion when spray button is pressed to avoid runs and sags.
Apply a single, thin layer and avoid application of thick layers. After use turn can upside down and press spray button for 2 - 3 seconds to clean valve.
For good results the relative humidity shall be below 85% and the temperature of the can and substrate above 0°C.