- product information
A fast drying zinc rich primer based on an epoxy ester resin. Zinc Spray 2185 is intended to be applied on small areas or for touch-up.
Should be used on new, bare steel or galvanised steel surfaces.
The product contains pure zinc as pigment and provides cathodic protection.
The product can be recoated with non-saponifiable coatings. Zinc Spray 2185 should be used as a primer or as a single coat in light industrial exposures, corrosive environments and high humidity areas.
- technical specifications
Size 500ml For use on
New, bare steel, blasted steel or galvanized steel surfaces
Appearance Matt Drying times 20°C/50% r.v. To touch
10 Minutes Drying times 20°C/50% r.v. To Recoat Within 1 hour or after 48 hours Binder Epoxy ester Heat Resistance n/a Theoretical Coverage1.7 m² per spay can at 25 μm dry 1.4 m² per spay can at 35 μm dry MPN 2185 GTIN
- • Matt grey appearance
- • 90% zinc in the dry film (99% pure zinc)
- • To protect bare, rust free metal and galvanised
- • Ideal for touching-up welding seams
- • Conforms to DIN 50.976 (1983)
- • Resists 500 hours of salt spray testing (DIN)
Remove dirt, grease, oil, loose rust and all other surface contaminants by appropriate means.
The surface must be clean and dry during application.
DIRECTION FOR USE
Remove cover cap. Shake vigorously for at least one minute after the rattle of mixing ball is heard.
Shake frequently during use. Hold can at least 25 cm from surface.
Use back and forth motion keeping can parallel with surface. Ensure that can is in motion when spray button is pressed to avoid runs and sags.
Apply a single, thin layer and avoid application of thick layers. After use turn can upside down and press spray button for 2 - 3 seconds to clean valve.
For good results the relative humidity shall be below 85% and the temperature of the can and substrate above 0°C.